|Appearance:||White Powder||Solid Content:||≥88%|
|Molecular Weight:||10-25(million)||Dissolving Time:||≤60(min)|
|Specific Gravity At 25°C::||1.01-1.1||Sample:||Test Free|
Wastewater Purification Anionic Polyacrylamide Flocculation Polyelectrolyte Metallic Nickel
Raitte A4520 Grade Specifications:
|Appearance:||Off-White Granular Powder|
|Particle Size:||20-100 mesh|
|Molecular Weight:||5-25 million|
|Solid Content:||89% Min|
|Approximate Brookfield viscosity at 25° C:||@ 1.0%||>1500|
|Bulk Density:||About 0.6-0.8|
|Specific Gravity at 25°C:||1.01-1.1|
|PH (1% aqua solution):||6-9|
|Storage Temperature (°C):||0 - 35|
|Shelf Life:||2 years|
|As flocculants for raw water sedimentation, thickening, and suspending removal|
Used for acidophilic water systems. If matched with PAC, aluminum sulfate,
the effect will be excellent.
Dosing polyacrylamide can reduce the consumption of coagulant and speed up
|Coal washing tailing centrifugal separation
Sedimentation and filtration of coal powder and coal mud.
Highly improve the recovery rate of coal powder and the filtration speed.
Used as a fixing agent, residency agent, filtration aid, and paper dry and wet
intensity reinforcing agent in the paper-making industry.
|Dissolved into 0.3% concentration and cross-linking agent added. It can be sprayed on deserts to prevent and solidify sand.|
Oil field profile controlling and water-plugging agent, matched with lignocellulose
and a certain amount of chemical adhesive added. It can be used as an oil field profile
controlling and water-plugging agent.
In the oil fields, as a kind of mud additive.
To increase the viscosity of water and improve the effectiveness of the water flooding
|For sugar and juice flocculation, sedimentation, clarification, and floatation|
|10||Soil humectants||It can preserve water and solidify sand for soil and can play the role of humectant on 1|
Textile Sizing, as a kind of composition for chemical grout, starch textiles
Highly improve the adhesive property, penetrability, and desizing performance, enable the textile to have electrostatic prevention performance, reduces the desizing rate, and reduces the starch mixing spots, cloth machine breaking efficiency, and falling objects.
|1||Medium Molecular Weight and high Charge Degree.|
|2||Economical to use - lower dosage levels.|
|3||For Water treatment as a flocculant to make flocs|
|4||Easily soluble in water; dissolves rapidly.|
|5||Noncorrosive of suggested dosage, economical, and effective at low levels.|
|6||10 years of manufacturing experience, with more than 20 technical engineers|
Adsorbing suspension particles, polymer chains entangle and cross-link each other to form bridging and make flocculation structure enlarge and thicken, and have the functions of surface adsorption and electric neutralization.
PAM molecule chain and dispersed phase form bridging bonds, ion bonds, and covalent bonds to increase combination strength.
|Polyacrylamide (polyelectrolyte/flocculant) should be standardly dissolved to 0.1-0.5% concentration.|
|The time required to dissolve the flocculant varies according to the type of flocculant, water quality, temperature, and agitation. However, most flocculants generally require around 1 hour of agitation to completely dissolve the powder. An incomplete mixture of flocculants or lumping may inhibit the performance of the flocculant.|
|The ideal revolution of the agitator is between 200-400rpm. A high-speed agitator operating without reducing the revolution of a motor is not advised, since it may cut the molecules of the flocculant. An ideal agitator motor should be 1HP for a 1-2m3 mixing tank.|
|The dosage range varies from 1 - 3.0 ppm depending upon the type of effluent and application. Advised to do jar tests for evaluating the functioning and approximate dosage.|
|5||Jar Test:||Put a sample of effluent in a beaker and add it as designated, agitate for 1 minute at 100-120 rpm and then slowly agitate at 60rpm. Determine the flocs properly at this time and note the sedimentation and clarity of the top solution.|